緊固件機械性能 不銹鋼和鎳合金緊固件選用指南 GB /T 3098.25 - 2020

---

• 

  表1 奧氏體不銹鋼化學成分（GB/T 3098.6、GB/T3098.15、GB/T 3098.16、GB/T3098.21）

  
  

  
  

  ISO代號	化學成分（質量分數）a / %												對應的緊固件組別b
  	C	Si	Mn	P	S	Cr	Mo	Ni	Cu	N	Nb	Ti
  奧氏體不銹鋼
  4305-303-00-I	0.120	1.00	2.00	0.060	≥0.15	17.0~19.0	/	8.0~10.0	1.0	0.10	/	/	A1
  4301-304-00-I	0.070	1.00	2.00	0.045	0.030	17.5~19.5	/	8.0~10.5	/	0.10	/	/	A2
  4307-304-03-I	0.030	1.00	2.00	0.045	0.030	17.5~19.5	/	8.0~10.5	/	0.10	/	/	A2L
  4311-304-53-I	0.030	1.00	2.00	0.045	0.030	17.5~19.5	/	8.0~11.0	/	0.12~0.22	/	/	A2L
  4567-304-98-X	0.080	1.00	2.00	0.045	0.030	17.0~19.0	/	8.0~10.5	1.0~3.0	/	/	/	A2
  4567-304-30-I	0.040	1.00	2.00	0.045	0.030	17.0~19.0	/	8.0~10.5	3.0~4.0	0.10	/	/	A3
  4541-321-00-I	0.080	1.00	2.00	0.045	0.030	17.0~19.0	/	9.0~12.0	/	/	/	5×C~0.70	A3
  4550-347-00-I	0.080	1.00	2.00	0.045	0.030	17.0~19.0	/	9.0~12.0	/	/	10×C~1.00	/	A3
  4401-316-00-I	0.080	1.00	2.00	0.045	0.030	16.0~18.0	2.00~3.00	10.0~13.0	/	0.10	/	/	A4
  4404-316-03-I	0.030	1.00	2.00	0.045	0.030	16.5~18.5	2.00~3.00	10.0~13.0	/	0.10	/	/	A4L
  4406-316-53-I	0.030	1.00	2.00	0.045	0.030	16.5~18.5	2.00~3.00	10.0~12.5	/	0.12~0.22	/	/	A4L
  4578-316-76-E	0.040	1.00	2.00	0.045	0.015	16.5~17.5	2.00~2.50	10.0~11.0	3.0~3.5	0.10	/	/	A4
  4571-316-35-I	0.080	1.00	2.00	0.045	0.030	16.5~18.5	2.00~2.50	10.5~13.5	/	/	/	5×C~0.70	A5
  4529-089-26-I	0.020	0.75	2.00	0.035	0.015	19.0~21.0	6.0~7.0	24.0~26.0	0.5~1.5	0.15~0.25	/	/	A8
  4547-312-54-I	0.020	0.70	1.00	0.035	0.015	19.5~20.5	6.0~7.0	17.5~18.5	0.50~1.00	0.18~0.25	/	/	A8
  4478-083-67-U	0.030	1.00	2.00	0.040	0.030	20.0~22.0	6.0~7.0	23.5~25.5	0.75	0.18~0.25	/	/	A8
  注：表中所列成分除標明范圍或最小值外，其余均為最大值。
  a 未經買方同意，不宜將未規定的元素加入鋼材中，除非為了完成冶煉。應采取一切合理的預防措施，以防止從制造中使用的廢料或其他材料中添加影響淬透性、機械性能和適用性的元素。 b 鋼的組別與GB/T 3098.6和GB/T 3098.15規定的成分范圍最接近，但是，本表中包含的不一定完全符合。

  
  

• 

  表2 馬氏體、鐵素體和雙相鋼化學成分（GB/T 3098.6、GB/T 3098.15、GB/T 3098.16、GB/T 3098.21)

  
  

  
  

  ISO代號	化學成分（質量分數）a / %												對應的緊固件組別b
  	C	Si	Mn	P	S	Cr	Mo	Ni	Cu	N	Nb	Ti
  馬氏體不銹鋼
  4006-410-00-I	0.08~0.15	1.00	1.5	0.040	0.030	11.5~13.5	/	0.75	/	/	/	/	C1
  4021-420-00-I	0.16~0.25	1.00	1.50	0.040	0.030	12.0~14.0	/	/	/	/	/	/	C1
  4028-420-00-I	0.26~0.35	1.00	1.50	0.040	0.030	12.0~14.0	/	/	/	/	/	/	C1
  4057-431-00-X	0.12~0.22	1.00	1.50	0.040	0.030	15.0~17.0	/	1.50~2.50	/	/	/	/	C3
  4005-416-00-I	0.08~0.15	1.00	1.50	0.040	≥0.15	12.0~14.0	0.60	/	/	/	/	/	C4
  鐵素體不銹鋼
  4016-430-00-I	0.08	1.00	1.00	0.040	0.030	16.0~18.0	/	/	/	/	/	/	F1
  雙相不銹鋼
  4482-320-01-X	0.030	1.00	4.0~6.0	0.035	0.030	19.5~21.5	0.10~0.60	1.50~3.50	1.0	0.05~0.20	/	/	D2d
  4362-323-04-I	0.030	1.00	2.00	0.035	0.015	22.0~24.5	0.10~0.60	3.5~5.5	0.10~0.60	0.05~0.20	/	/	D2d
  4062-322-02-U	0.030	1.00	2.00	0.040	0.010	21.5~24.0	0.45	1.00~2.90	/	0.16~0.28	/	/	D4
  4162-321-01-E	0.040	1.00	4.0~6.0	0.040	0.015	21.0~22.0	0.10~0.80	1.35~1.90	0.10~0.80	0.20~0.25	/	/	D4
  4662-824-41-X	0.030	0.70	2.50~4.0	0.035	0.005	23.0~25.0	1.00~2.00	3.0~4.5	0.10~0.80	0.20~0.30	/	/	D4
  4462-318-03-I	0.030	1.00	2.00	0.035	0.015	21.0~23.0	2.5~3.5	4.5~6.5	/	0.10~0.22	/	/	D6
  4481-312-60-J	0.030	1.00	1.50	0.040	0.030	24.0~26.0	2.5~3.5	5.5~7.5	/	0.08~0.30	/	/	D6
  4410-327-50-E	0.030	1.00	2.00	0.035	0.015	24.0~26.0	3.0~4.5	6.0~8.0	/	0.24~0.35	/	/	D8
  4501-327-60-I c	0.030	1.00	1.00	0.030	0.010	24.0~26.0	3.0~4.0	6.0~8.0	0.5~1.0	0.20~0.30	/	/	D8
  4507-325-20-I	0.030	0.70	2.00	0.035	0.015	24.0~26.0	3.0~4.0	6.0~8.0	1.0~2.5	0.20~0.30	/	/	D8
  注：表中所列成分除標明范圍或最小值外，其余均為最大值。
  a 未經買方同意，不宜將未規定的元素加入鋼材中，除非為了完成冶煉。應采取一切合理的預防措施，以防止從制造中使用的廢料或其他材料中添加影響淬透性、機械性能和適用性的元素。 b 鋼的組別與GB/T 3098.6和GB/T 3098.15規定的成分范圍最接近，但是，本表中包含的不一定完全符合。 c 鎢的含量應為0.5%~1.0%。 d 當wCr＋3.3wMo＋16wN＞24和符合GB/T 3098不銹鋼系列標準時，可被認同為D4。

  
  
  
• 

  表3 高溫不銹鋼和鎳合金化學成分（GB/T 3098.6、GB/T 3098.15、GB/T 3098.16、GB/T 3098.21）

  
  

  
  

  ISO代號	化學成分（質量分數）a / %												對應的緊固件組別b
  	C	Si	Mn	P	S	Cr	Mo	Ni	Cu	N	Nb	Ti
  馬氏體不銹鋼
  4021-420-00-I	0.16~0.25	1.00	1.50	0.040	0.030	12.0~14.0	/	/	/	/	/	/	CH0
  4028-420-00-I	0.26~0.35	1.00	1.50	0.040	0.030	12.0~14.0	/	/	/	/	/	/	CH1
  4057-431-00-X	0.12~0.22	1.00	1.50	0.040	0.030	15.0~17.0	/	1.50~2.5	/	/	/	/	CH2
  4923-422-77-Ec	0.18~0.24	0.50	0.40~0.90	0.025	0.015	11.0~12.5	0.8~1.2	0.30~0.80	/	/	/	/	V或VH
  1.4913d	0.17~0.23	0.50	0.40~0.90	0.025	0.015	10.0~11.5	0.50~0.80	0.20~0.60	/	0.05~0.10	0.25~0.55	/	VW
  奧氏體沉淀硬化不銹鋼和鎳合金
  4980-662-86-Xc	0.08	1.00	2.00	0.040	0.030	13.5~16.0	1.0~1.5	24.0~27.0	/	/	/	1.90~2.35	SD
  2.4952f	0.04~0.10	1.00	1.00	0.020	0.015	18.0~21.0	/	≥65	0.20	/	/	1.80~2.70	SB
  2.4668g	0.02~0.08	0.035	0.035	0.015	0.015	17.0~21.0	2.80~3.30	50.00~55.00	0.30	/	/	0.60~1.20	718
  注：表中所列成分除標明范圍或最小值外，其余均為最大值。
  a 未經買方同意，不宜將未規定的元素加入鋼材中，除非為了完成冶煉。應采取一切合理的預防措施，以防止從制造中使用的廢料或其他材料中添加影響淬透性、機械性能和適用性的元素。 b 鋼的組別與GB/T 3098.6和GB/T 3098.15規定的成分范圍最接近，但是，本表中包含的不一定完全符合。 c 此外，釩的含量應為0.25%~0.35%。 d 化學成分與EN 10269一致；此外，鋁含量應≤0.020%，釩含量應為0.10%~0.30%，硼含量≤0.0015%。 e 此外，鋁含量應≤0.35%，釩含量應為0.10%~0.50%，硼含量0.001%~0.010%。 f 化學成分與EN 10269一致；此外鋁含量應為1.00%~1.80%，鈷含量應≤1.00%，鐵含量≤1.50%，硼含量≤0.008%。 g 化學成分與EN 10269一致；此外鋁含量應為0.30%~0.70%，鈷含量應≤1.00%，硼含量0.002%~0.006%，鈮含量應為4.7%~5.50%（其余為鐵）。

  
  

---

• 

  表A.1 冷鐓緊固件用主要不銹鋼常用牌號一奧氏體等級

  
  

  表A.1 冷鐓緊固件用主要不銹鋼常用牌號一奧氏體等級^a

  類別	組別h	ISO 15510代號	歐洲材料		ASTM標準中代號	美國常用牌號	GB/T 3098 系列標準中位置	GB/T 20878中代號	相關標準
  			代號	牌號
  加硫奧氏體	A1	4305-303-00-I	1.4305	X8CrNiS18-9	S30300	303	第 5 章，表1	S30317	ASTM A959，EN 10088-3
  	A1	4570-303-31-I	1.4570	X6CrNiCuS18-9-2	S30331	303Cu	GB/T 3098.6 GB/T 3098.15	-	EN 10088-3
  一般用途 奧氏體 一般用途奧氏體	A2L	4307-304-03-I	1.4307	X2CrNi18-9	S30403	304L	第 5 章，表1	S30403	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
  	A2L	4306-304-03-I	1.4306	XZCrNi19-11	S30403	304L	GB/T 3098.6 GB/T 3098.15	S30403	ASTM A959，EN 10088-3，EN 10263-5
  	A2L	4311-304-53-I	1.4311	X2CrNiN18-9	S30453	304LN	第5章，表1	S30453	ASTM A959，EN 10088-3
  	A2	4311-304-00-I	1.4301	X5CrNi18-10	S30400	304	第5章，表1	S30408	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
  	A2	4567-304-30-I	1.4567c	X3CrNiCu18-9-4	S30430	304Cu	第5章，表1	S30488	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
  	A2	4560-304-75-E	1.4560	X3CrNiCu19-9-2	-	304Cu	GB/T 3098.6 GB/T 3098.15		EN 10088-3，EN 10263-5
  	A2	4303-305-00-I	1.4303	X4CrNi18-12	S30500	305	GB/T 3098.6 GB/T 3098.15	S30510	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
  	A3	4550-347-00-I	1.4550	X6CrNiNb18-10	S34700	347	第5章，表1	S34778	EN 10088-1
  	A3	4541-321-00-I	1.4541	X6CrNiTi18-10	S32100	321	第5章，表1	S32168	ASTM A959，EN 10088-3，EN 10263-5
  	d	4615-201-75-E	1.4615	X3CrMnNiCu15-8-5-3		201Cu			EN 10088-3
  	d	4310-301-00-I	1.4310	Xl0CrNi18-8	S30100	301		S30110	ASTM A959，EN 10088-3，EN 10263-5
  含鉬奧氏體	A4	4401-316-00-I	1.4401	X5CrNiMo17-12-2	S31600	316	第5章，表1	S31608	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
  	A4L	4404-316-03-I	1.4404	X2CrNiMo17-12-2	S31603	316L	第5章，表1	S31603	ASTM A959，EN 10088-3，EN 10263-5，EN 10269
  	A4L	4406-316-53-I	1.4406	X2CrNiMoN17-11-2	S31653	316LN	第5章，表1	S31653	ASTM A959，EN 10088-3
  	A4L	4432-316-03-I	1.4432	X2CrNiMo17-12-3	S31603	316L	GB/T 3098.6 GB/T 3098.15	S31603	ASTM A959，EN 10088-1，EN 10263-5
  	A4L	4435-316-91-I	1.4435	X2CrNiMo18-14-3	S31603	316L	GB/T 3098.6 GB/T 3098.15	S31603	ASTM A959，EN 10088-3
  	A4	4436-316-00-I	1.4436	X3CrNiMo17-13-3	331600	316	GB/T 3098.6 GB/T 3098.15	S31608	GB/T 20878，ASTM A959，EN 10088-3，EN 10263-5
  	A4	4578-316-76-E	1.4578	X3CrNiCuMo17-11-3-2			第5章，表1		EN 10088-3，EN 10263-5
  	A5	4571-316-35-I	1.4571	X6CrNiMoTi17-12-2	S31635	316T1	第5章，表1	S31668	ASTM A959，EN 10088-3，EN 10263-5
  高鉬超級奧氏體	AS	4478-083-67-U	1.4478	X2NiCrrMoN25-21-7	N08367		第5章，表1		ASTM A959，EN 10088-1
  	AS	4529-089-26-I	1.4529	XlNiCrMoCuN25-20-7	N08926	926	第5章，表l		ASTM A959，EN 10088-1
  	AS	4547-312-54-I	1.4547	XlCrNiMoCuN20-18-7	S31254	F44	第5章，表1	S31252	ASTM A959，EN 10088-1
  特殊用途高合金奧氏體	SDe.f	4980-662-86-X	1.4980	X6NiCrTiMoVB25-15-2	S66286	A286 合金 660	GB/T 3098.8 GB/T 3098.24 第5章，表3	S51525 GH2132 (GB/T 14992)	ASTM A959，EN 10088-3，EN 10269，DIN 267-13
  	Se		1.4986	X7CrNiMoBNb16-16			GB/T 3098.8		EN 10088-1，EN 10269，DIN 267-13
  	d	4539-089-04-l	1.4539	XlNiCrMoCu25-20-5	N08904	904L		S39042	ASTM A959，EN 10088-3
  	d	4841-314-00-E	1.4841	Xl5CrNiSi25-21	S31400	314			ASTM A959，EN 10088-1
  	d	4828-305-09-l	1.4828	Xl5CrNiSi20-12					ASTM A959，EN 10088-1
  	d	4845-310-08-E	1.4845	X8CrNi25-21	S31008	310S		S31008	ASTM A959，EN 10088-1
  高錳超級奧氏體	d	4020-241-00-X	1.4020	Xl3CrMnNiN18-13-2	S24100	XM28			ASTM A959，EN 10088-3
  	d	4378-240-00-X	1.4378	X6CrMnNiNl8-13-3	S24000	XM29			ASTM A959，EN 10088-3
  高鎳超級奧氏體	SBe，f		2.4952	NiCr20TiAl	N07080	合金80A	GB/T 3098.24	GH4080A (GB/T 14992)	ASTM B637，EN 10269，DIN 267-13
  	718f		2.4668	NiCr19NbMo	N07718	合金718	GB/T 3098.24	GH4169 (GB/T 14992)	ASTM B637，EN 10269，DIN 267-13
  a 各種標準的組成之間沒有確切的對應關系，但多數重疊 。 b 組別符合GB/T 3098中不銹鋼機械性能系列標準規定。 c 根據EN 10263-5，鎳最低含量通常為8% 。 d 特殊等級，在GB/T 3098.6、GB/T 3098.15或GB/T 3098.8 中未規定。 e 代號符合GB/T 3098.8。 f  由GB/T3098.24規定 的 。

   

  
  
• 

  表A.2 冷鐓緊固件用主要不銹鋼常用牌號一鐵素體、馬氏體和雙相鋼等級

  
  

  表A.2 冷鐓緊固件用主要不銹鋼常用牌號一鐵素體、馬氏體和雙相鋼等級^a

  類別	組別b	ISO 15510代號	歐洲材料		ASTM標準中代號	美國常用牌號	GB/T 3098系列標準中位置	GB/T 20878中代號	相關標準
  			代號	牌號
  一般用途馬氏體鋼	C1	4006-410-00-I	1.4006	X12Cr13	S41000	410	第5章，表2	S41010	ASTM A959 ，EN 10088-3，EN 10263-5
  	C1	4000-410-08-I	1.4000	X6Cr13	S41008	410S	GB/T 3098.6 GB/T 3098.15	S41008	ASTM A959，EN 10088-3
  	C1，CH0c	4021-420-00-I	1.4021	X20Cr13	S42000	420	第5章，表2 GB/T 3098.6 GB/T 3098.15 GB/T 3098.24	S42020	ASTM A959，EN 10088-3
  	C1，CH1c	4028-420-00-I	1.4028	X30Cr13	S42000	420	第5章，表2 GB/T 3098.6 GB/T 3098.15 GB/T 3098.24	S42030	ASTM A959 ，EN 10088-3
  	C1	4034-420-00-I	1.4034	X46Cr13	S42000	420	GB/T 3098.6 GB/T 3098.15	S42040	ASTM A959，EN 10088-3
  	d	4003-410-77-I	1.4003	X19CrMoNbVN11-1	S41003			S11213	ASTM A959，EN 10088-1
  	VWc，e		1.4913	X19CrMoNbVN11-1			GB/T 3098.8 GB/T 3098.24		EN 10088-1，EN 10269，DlN 267-13
  	V或VHc，e	4923-422-77-E	1.4923	X22CrMoV12-1			第5章，表3 GB/T 3098.8 GB/T 3098.24		EN 10088-1，EN 10269，DIN 267-13
  高鉻馬氏體	C3，CH2c	4057-431-00-X	1.4057	X17CrNi16-2	S43100	431	第5章，表3 GB/T 3098.24	S43120	ASTM A959，EN 10088-3
  	d	4542-174-00-I	1.4542f	X5CrNiCuNb16-4	S17400	17-4PH		S51740	ASTM A959，EN 10088-3
  	d	4418-431-77-E	1.4418	X4CrNiMo16-5-1					EN 10088-3
  	d	4122-434-09-I	1.4122	X39CrMo17-1					EN 10088-3
  加硫馬氏體	C4	4005-416-00-I	1.4005	X12CrS13	S41600	416	第5章，表2	S41617	ASTM A959，EN 10088-3
  	C4	4029-420-20-I	1.4029	X29CrS13	S42020	420F	GB/T 3098.6， GB/T 3098.15	S42037	ASTM A959，EN 10088-3
  鐵素體	F1	4016-430-00-I	1.4016	X6Cr17	S43000	430	第5章，表2	S11710	ASTM A959，EN 10088-3，EN 10263-5
  	F1	4511-430-71-I	1.4511	X3CrNb17			GB/T 3098.6， GB/T 3098.15		EN 10088-3
  	F1	4113-434-00-I	1.4113	X6CrMo17-1	S43400	434	GB/T 3098. 6， GB/T 3098.15	S11790	ASTM A959，EN 10088-3，EN 10263-5
  	F1	4526-436-00-I	1.4526	X6CrMoNb17-1	S43600	436	GB/T 3098. 6， GB/T 3098.15	S11770	ASTM A959，EN 10088-3
  	F1	4509-439-40-X	1.4509	X2CrT iNb18	S43940	441	GB/T 3098.6， GB/T 3098.15	S11873	ASTM A959，EN 10088-3
  	F1	4521-444-00-I	1.4521	X2CrMoTi18-2	S44400	444	GB/T 3098.6， GB/T 3098.15	S11972	ASTM A959，EN 10088-2
  加硫鐵素體	d	4004-430-20-I	1.4004	X7CrS17	S43020	430F		S11717	ASTM A959，EN 10088-1
  	d	4019-430-20-I	1.4104	X14CrMoS17	S43020	430F			ASTM A959，EN 10088-3
  雙相鋼	D2 g	4482-320-01-X	1.4482h	X2CrMnNiMoN21-5-3	S32001	2001	第5章，表2， GB/T 3098.6， GB/T 3098.15		ASTM A959，EN 10088-3
  	D2g	4362-323-04-I	1.4362h	X2CrNiN23-4	S32304	2304	第5章，表2， GB/T 3098.6， GB/T 3098.15		ASTM A959，EN 10088-3
  	D4	4162-321-01-E	1.4162 h	X2CrMnNiN21-5-1	S32101	2101	第5章，表2 GB/T 3098.6， GB/T 3098.15	S23043	ASTM A959，EN 10088-3
  雙相鋼	D4	4062-322-02-U	1.4062h	X2CrNiN22-2	S32202	2202	第5章，表2， GB/T 3098.6， GB/T 3098.15		ASTM A959，EN 10088-3
  	D6	4462-318-03-I	1.4462	X2CrNiMoN22-5-3	S31803 S32205	1803,2205	第5章，表2， GB/T 3098.6， GB/T 3098.15	S22053	ASTM A959，EN 10088-3，EN 10263-5
  	D6	4481-312-60-J	1.4481	X2CrNiMoN25-7-3	S31260	SUS329J4Li	第5章，表2， GB/T 3098.6， GB /T 3098.15	S22583	ASTM A959，EN 10088-1
  	D8	4410-327-50-E	1.4410	X2CrNiMoN25-7-4	S32750	2507	第5章 ，表2， GB/ T 3098.6， GB/ T 3098.15	S25073	ASTM A959，EN 10088-3
  	D8	4501-327-60-I	1.4501	X2CrNiMoCuWN25-7-4	S32760	-	第5章，表2， GB/T 3098.6， GB/T 3098.15	S27603	ASTM A959，EN 10088-3
  	D8	4507-325-20-I	1.4507	X2CrNiMoCuN25-6-3	S32520	-	第5章，表2， GB/T 3098.6， GB/T 3098.15	S25554	ASTM A959，EN 10088-3
  a 各種標準的組成之間沒有確切的對應關系，但多數重疊。 b 組別符合GB/T 3098中不銹鋼機械性能系列標準規定。 C 由GB/T 3098.24規定的代號。 d 特殊等級，在GB/T 3098.6，GB/T 3098.15或 GB/ T 3098.8中未規定。 e代號符合GB/T 3098.8。 f所謂的沉淀硬化等級( PH ) 是低碳、改善韌性和耐腐蝕性的馬氏體鋼。 g 當ωCr + 3.3ω Mo + 16ωN > 24.0 和符合GB/T 3098不銹鋼系列標準時，可被認同為D4。 h 所謂的“低雙相”鋼等級，鎳和鉬含顯較低。 j 根據JIS G 4308。